Modern Jewelry Designs

Of gold’s properties, when it was first discovered (probably in Mesopotamia before 3000 BCE), it was the metal’s malleability that was a new phenomenon: the only beeswax, when heated to a certain temperature, could be compared to it. Gold’s molecules move and change position in accordance with the stresses to which it is submitted, so that when it is beaten it gains in the surface area what it loses in thickness. In modern jewelry, gold can take on a variety of hues when it is alloyed with other metals: water green, white, gray, red, and blue.

Metalwork

The basic components of jewelry have always consisted of sheet metal, metal cast in a mold, and wire (more or less heavy or fine). These components take on the desired shape by means of techniques carried out with the help of tools. Gold in its natural state was beaten while hot or cold and reduced to extremely thin sheets (this operation could be performed with stone hammers). The sheets were then cut into the desired sizes.

Examination of the most ancient pieces of jewelry shows that one of the techniques used most widely in decorating metal sheets for jewelry was embossing (relief work). Throughout the centuries embossing techniques have remained substantially unchanged, although in modern times mechanization has made possible mass production of decorative parts of jewelry, with great savings of time and labour but with a corresponding lack of art.

In repoussé, the relief is pressed (in a negative mold) or hammered out from the reverse side of the gold sheet and then finished off on the right side with a hammer or engraving tool. For half-modeled or completely round reliefs, the gold leaf was pressed onto wooden or bronze models. Completely round objects were made in two pieces and then welded together.

Another embossing, or relief, the technique is engraving, which involves impressing designs into the metal with a sharp tool.

Decorative openwork designs can be created by piercing the gold leaf. In the Roman period, this technique was called opus interactive.

Granulation is a decorative technique in which small or minute gold balls (with diameters ranging from 1/60 to 1/180 of an inch) are used to form silhouettes on smooth or embossed metal.

Casting from precious metals has always been rare. When the relief was to be visible only from one side, the metal was poured into the cast and, when hardened, touched up with a graver. When the relief was to be fully modeled, the cire perdue (lost-wax) process, involving casting from a wax mold, was used.

Gold and silver wire, according to its function, can be made into various sizes, shapes, sections, and weights. It can serve to join, to support pendants of varying importance, to make necklaces and bracelets, or to alternate with other decorative components.

From the 3rd millennium BCE through the present day, chains—ranging from the simple type, consisting of a series of round or oval rings, to one of the oldest elaborations, the “loop in loop,” or square, chain—have offered goldsmiths the widest field for decorative imagination.